Fatigue Studies On Aluminum 6061/SiC Reinforcement Metal Matrix Composites
DOI:
https://doi.org/10.18311/jmmf/2022/30684Keywords:
Fatigue, forging, wohler curves, silicon carbide, reinforcement.Abstract
Fatigue is a process of progressive localized plastic deformation occurring in a material subjected to cyclic stresses and strains at high stress concentration locations that may culminate in cracks or complete fracture after a sufficient number of fluctuations. Fatigue testing is carried out using the ASTM D3479 with a notch or crack for investigating the initiation of crack. Several fatigue tests were conducted in tension-tension and/or tensioncompression loading at a frequency of 10Hz or sinusoidal wave’s frequency of 5Hz, and at constant-amplitude. The fatigue tests were interrupted by the researchers at regular intervals after a predetermined number of cycles to monitor crack advance and to observe the failure modes by various ways such as visual observation, digital camera, traveling microscope, CCD camera, etc.
Downloads
Metrics
Downloads
Published
How to Cite
Issue
Section
Accepted 2022-07-12
Published 2022-07-12
References
Piramanayagam, Sethu Ramalingam, Prabhakar M., Mayandi K., C.S Mahalakshmi, G Manigandan, P Mouleeshwaran and Kanna S.K. Rajesh (2020): Developing a Rotating Fatigue Test Machine and Testing with Dissimilar Materials. Journal of Advanced Research in Dynamical and Control Systems. 12. 631-638. 10.5373/ JARDCS/V12SP5/20201798.
Jones D. (1987): Fatigue test machine. Patent Application Department of the Air Force, Washington, DC..
Macek Wojciech, Zawioelak Stanis³aw, Deptu³a Adam and Ulewicz Robert. (2019): Fatigue Testing Machines and Apparatus. Quality Production Improvement. 10. 80-108. 10.30657/qpi.2019.10.08.
Meggiolaro Marco, Castro Jaime and Nogueira Rodrigo. (2017): A Fast Rotating Bending Fatigue Test Machine. 10.26678/ABCM.COBEM2017.COB17-1824.
Macek Wojciech, Zawioelak Stanis³aw, Deptu³a Adam and Ulewicz Robert. (2019): Fatigue Testing Machines and Apparatus. Quality Production Improvement. 10. 80-108. 10.30657/qpi.2019.10.08.
IIJIMA Noriko, Honma Shinya, Ryotaro Nakano, Hayashi Shota, Hirano Tomoki, Iijima Toshihiko and Yajima Yasutomo (2021): Fatigue properties of hollow zirconia implants. Dental Materials Journal. 40. 10.4012/dmj.2020-248.
Peng Zi, Sheng Jun, Wang Xu and Tang Yue. (2021): Low Cycle Fatigue Properties of FGH720Li Superalloy. Materials Science Forum. 1035. 292-296. 10.4028/ www.scientific.net/MSF.1035.292.
Liu Chi, Ma Liyong, Zhang Ziyong, Fu Zhuo and Liu Lijuan. (2021): Research on the Corrosion Fatigue Property of 2524-T3 Aluminum Alloy. Metals. 11. 1754. 10.3390/met11111754.
Bai Yishan, Yang Shanglei, Zhu Minqi and Fan Cong. (2021): Study on Microstructure and Fatigue Properties of FGH96 Nickel-Based Superalloy. Materials. 14. 6298. 10.3390/ma14216298.
Lee J.H. and Cho Jaeung. (2017): A Fatigue Fracture Study on TDCB Aluminum Foam Specimen of Type Mode III Bonded with Adhesive. Archives of Metallurgy and Materials. 62. 10.1515/amm-2017-0208.
Hadzihafizovic Dzevad. (2021): Fatigue fractures. 10.13140/RG.2.2.11744.81929.
González-Velázquez Jorge. (2018:. Fatigue Fracture. 10.1007/978-3-319-76651-5_4.